Исследование свойств хрома, получаемого способом гальванохонингования
| Раздел |
[RUS] Электроосаждение металлов и сплавов [ENG] Electroplating of metals and alloys |
| Страницы | 41-45 |
| Тип | [RAR] - Научная статья |
| Коды | |
| Заглавие |
[RUS] Исследование свойств хрома, получаемого способом гальванохонингования [ENG] Study of Chromium Coatings Properties Deposited by Galvanohoning Method |
| Авторы |
[RUS] Ким Вячеслав Елисеевич 195248, Санкт-Петербург, Уманский пер., д. 71 galvanochrom@yandex.ru ООО «ГальваноХром» Телефон +7 (812) 226-03-63; +7 (812) 336-93-82 [ENG] Kim V.E. 195248, Saint-Petersburg, Russia, 71 Umanskiy alleyway Galvanochrom Ltd [RUS] Макеенко Е.Я. 195248, Санкт-Петербург, Уманский пер., д. 71 ООО «ГальваноХром» Телефон +7 (812) 226-03-63; +7 (812) 336-93-82 [ENG] Makeenko E.Ya. 195248, Saint-Petersburg, Russia, 71 Umanskiy alleyway Galvanochrom Ltd [RUS] Васильевский Василий Васильевич 195248, Санкт-Петербург, Уманский пер., д. 71 ООО «ГальваноХром» Телефон +7 (812) 226-03-63; +7 (812) 336-93-82 [ENG] Vasilievski V.V. 195248, Saint-Petersburg, Russia, 71 Umanskiy alleyway Galvanochrom Ltd |
| Аннотация |
[RUS] Исследовали свойства хромового покрытия, получаемого методом гальванохонингования. Показано, что покрытия могут иметь как свойства, присущие «штатному» хрому, так и комплекс оригинальных физико-химических характеристик, отличных от свойств хромовых покрытий. [ENG] Physico-mechanical characteristics of chromium coatings deposited by galvanohoning method have been studied. Two types of microstructure were observed; normal and stripped-type (Figs 2-4), the latter being probably related with the formation of multi-layer type of the deposit with the participation of compounds - products of uncomplete reduction of chromic acid. Apart from textured conventional chromium deposits which have tensile stress coatings obtained by galvanohoning have no texture and are characterized by compressive stress (Fig. 5 to 7). These deposits have hardness 600-1100 kg/ mm2 which does not depend on hone pressure (Fig.9) and is decreasing at higher current densities (Fig.8). Volume of hydrogen absorbed is reducing at higher current densities (Fig.10) and at higher hone pressure (curve 2 in Fig.11). Total amount of hydrogen absorbed is lower that in the case of conventional coatings. The new method of chromium plating has been proposed for the production of thick high-quality non-cracking bright coatings. |
| Текст | |
| Ключевые слова | |
| Ссылки |
Ким В.Е., Макеенко Е.Я., Васильевский В.В. Гальванотехника и обработка поверхности - 2008г. - 16, № 2, - С.24
А.Салли, Э. Брендз Хром. -М «Металлургия». 1971г.- 225 с. Лайнер В.И. Защитные покрытия металлов. -М: «Металлургия». 1974. - 410с. Ваграмян А.Т., Петрова Ю.С. Физико-механические свойства электролитических осадков. - М: АН СССР. 1960.- 164 с. |